Particle size analysis and elemental mapping providers with MicroVision Laboratories? Conclusion: Based on the analytical report, the client was able to demonstrate that the particles were consistent with a common aspirin tablet. When the end customer was approached with this report, they remembered that their spouse had taken an aspirin earlier that morning, and had likely used the bottle of water in question to do so. Based on this, the customer was happy, the manufacturing client was satisfied, and the sample was maintained – undestroyed should someone need to examine the sample again or do any more esoteric testing. For an affordable price, the client was able to get piece of mind, and gather information from a very wide range of testing methods quickly and accurately.

Light microscopy allows for the examination of optical and structural properties of a variety of samples. Optical properties such as polarization and birefringence help to differentiate between fibers, minerals, ceramics, biological materials and opaque materials including paints, coatings and metallic particles. This allows a wide range of particles to be quickly and effectively identified and quantified by an experienced analyst.

Do you do any animal testing? No. Do you analyze any tissue samples or blood samples? No. We do not do any blood analyses and we are not set up to prepare tissue samples. What are some of the cool samples you have looked at under the scanning electron microscope? We have seen 10,000 year old Wolly Mammoth hair, meteorites, an artificial heart valve, civil war bullets, insulin pumps, rare colonial coins, a kidney stone, and a few things we can’t talk about. But some of the more mundane samples, like wood or salt crystals, have proven to be extremely interesting subjects to image. Read more info on this page.

The profile of the flow of the solder at these bonds was documented using the SEM with backscatter imaging, which correlates brightness in the image with atomic density. Some voids were found in the solder as shown the SEM image. An EDS spectrum of the solder was acquired which showed that the solder was a tin/lead (80/20) solder. The EDS map clearly shows the copper wire and copper pad (red) with the tin lead solder (light blue) that appears to have flowed well and made a good bond between the copper elements. This map also shows the fiberglass bundles that add structural integrity to the board.

We are proud to announce that MicroVision Labs is now accredited to the ISO/IEC 17025:2017 standard. This represents over a year of diligent effort from all of our staff to verify and validate our in house SOP’s and transform our quality management system to one that is compliant to this international standard. This certification requires that accredited labs demonstrate that they are competent and can produce technically valid data and results unlike other certifications such as ISO 9001:2015. This represents an obvious value to our clients.

Examining the sample with a polarized light microscope (PLM), it was darker and coarser than expected for a mold sample. The dust appeared to be a closed cell, synthetic blown foam material, and all from the same source. The black color was likely due to pigment particles added to color the foam. Fourier Transform Infra-Red spectroscopy was performed on the foam particles. The spectrum showed a mixture of spectral features, associated with vinyl acetates, polyurethane, and cellulose or other sugar-like polymers. Based on these features, a common urethane acetate foam was determined as the likely source material. Explore even more details on https://microvisionlabs.com/.